| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
比浓度对数粘度(膜)d |
--- |
EMN-A-AC-G-V-1 |
0.70 |
--- |
| 试验膜厚度 |
--- |
D374 |
250微米(10mil) |
--- |
| 密度 |
--- |
D1505 |
1.27g/cm3 |
--- |
| 光雾 |
--- |
D1003 |
0.8% |
--- |
| 光泽 |
@45o |
D2457 |
108 |
--- |
| 透明度 |
--- |
D1746 |
85% |
--- |
| 一般透过率 |
--- |
D1003 改性 |
89% |
--- |
| 总透过率 |
--- |
D1003 改性 |
91% |
--- |
| 透湿率e |
--- |
F372 |
6g/m2?4h(0.4g/100in.2?4h) |
--- |
|
|
--- |
|
| 49 cm3 m/m2?4h tm(125 cm3 ll/100in.24h tm) |
| 10 cm3 m/m2?4h tm(25 cm3 ll/100in.24h tm) | |
--- |
| 物理性能 |
|
--- |
|
| 13.7N(1400gf) |
| 16.7N(1700gf) | |
--- |
|
|
--- |
|
|
--- |
| 抗撕裂传播,剖层撕裂方法 |
M.D. |
| M.D. |
| T.D. |
| T.D. | |
| @254mm/min(10in./min) |
| @254mm/min(10in./min) |
| @254mm/min(10in./min) |
| @254mm/min(10in./min) | |
|
| 9.1N(2.1 1bf) |
| 36N/mm(205 1bf/in.) |
| 9.1N(2.1 1bf) |
| 36N/mm(205 1bf/in.) | |
--- |
|
|
|
|
| 36N/mm(205 1bf/in.) |
| 36N/mm(205 1bf/in.) | |
--- |
|
|
--- |
|
| 52MPa(7500psi) |
| 52MPa(7500psi) | |
--- |
|
|
--- |
|
| 59MPa(8600psi) |
| 55MPa(8000psi) | |
--- |
|
|
--- |
|
|
--- |
|
|
--- |
|
|
--- |
|
|
--- |
|
| 1900MPa(2.8×105 psi) |
| 1900MPa(2.8×105 psi) | |
--- |
| 瞬间冲击f |
@23℃(73?H) |
| @-18℃(0?H) | |
--- |
|
|
--- |
| 机械性能 |
比重 |
--- |
ASTM D792 |
1.27 |
--- |